ASTM Threaded Metal Bar

ASTM Threaded Metal Bar

  • High Light

    ASTM Threaded Metal Bar

    ,

    ASTM Metal Threaded Rod

    ,

    12ft Threaded Metal Bar

  • Materials
    4140 /Hot Rolled/ Cold Rolled/ 40CrMo/ 42CrMo
  • Diameter
    1/2"-13 ~ 4"-8
  • Thread
    UN8 UNF
  • Grade
    B7 B7M B16
  • Coating
    Plain/ Black/ Zinc/ Hdg/ PTFE
  • Length
    12ft /3660mm
  • Product Name
    Metal Threaded Rod
  • Place of Origin
    China
  • Brand Name
    HAGER
  • Certification
    ISO9001:2015
  • Model Number
    1/4"-3-1/2",M6-M75
  • Minimum Order Quantity
    1000pcs
  • Price
    Inquiry
  • Packaging Details
    Bundles/cartons/pallets
  • Delivery Time
    15-30 Days
  • Payment Terms
    L/C, D/A, D/P, T/T, Western Union, MoneyGram
  • Supply Ability
    5000 tons per Month

ASTM Threaded Metal Bar

Metal Threaded Rod Stud Bar ASTM A193 Grade B7 B7M B16 "End to End" Class 2A

 

 

1.2 Use of water quenching is prohibited for any ferritic grade when heat treatment is performed after heading or threading.

 

1.3 Except as permitted below for B6X; bolting material that is subsequently cold drawn for dimensional control shall be stress-relieved after cold drawing. The minimum stress-relief temperature shall be within not more than 100 °F [55 °C] below the tempering temperature. Tests for mechanical prop-erties shall be performed after stress relieving.

 

1.4 B6 and B6X shall be held at the tempering tempera-ture for a minimum time of 1 h. B6X bolting material may be furnished in the as-rolled-and-tempered condition. Cold work-ing after heat treatment is permitted for B6X material provided the final hardness meets the requirements of Tables 2 and 3.

 

1.5 B7 and B7M shall be heat treated by quenching in a liquid medium and tempering. For B7M bolting components, such as bolts, studs, or screws, the final heat treatment, which may be the tempering operation if conducted at 1150 °F [620 °C] minimum, shall be done after all machining and forming operations, including thread rolling and any type of cutting. Surface preparation for hardness testing, nondestructive evaluation, or ultrasonic bolt tensioning is permitted.

 

1.5.1 Unless otherwise specified, bolting material for Grade B7 may be heat treated by the Furnace, the Induction or the Electrical Resistance method.

 

NOTE 4—Stress-relaxation properties may vary from heat lot to heat lot or these properties may vary from one heat-treating method to another. The purchaser may specify Supplementary Requirement S8, when stress-relaxation testing is desired.

 

1.6 Bolting material Grade B16 shall be heated to a temperature range from 1700 to 1750 °F [925 to 955 °C] and oil quenched. The minimum tempering temperature shall be as specified 

 

Product Name Stud Bar ASTM A193 Grade B7 B7M B16 "End to End" Class 2A
Size Diameter : M6-M100 ; Length : 5mm-5000mm
Standard B7 B7M B16
Brand DCT or According to customer's requirments
Finishing Plain, Black,Yellow/White Zinc Plated,H.D.G
Grade DIN: Gr 4.8, 8.8 ,10.9, 12.9 ; SAE: Gr2, 5, 8 ; ASTM:307A, 307B, A325, A394, A490, A449
Material Carbon Steel , Alloy Steel , Stainless Steel , Brass
Thread Type UNC, UNF, UNEF, METRIC,TR, ACME
Production Technique Cold forging, Hot forming, Maching, Heat Treatment ,ect
Production Capacity 1000 Tons per Month
Packaging Gross Weight about 25kgs per carton then 36 cartons per pallet or as customer's requirments
Certificate ISO9001;  API; 3.1.B
Trade Terms FOB , CIF, CNF,CFR,EXW
Terms of Payment T/T, L/C , Western Union , Paypal , Money Gram
Delivery Time Within 30days